Acrylic waterproof coating series water-based color multi-functional waterproof coating
1 product introduction
Acrylic waterproof coating (series water-based color multi-functional waterproof coating) is a one-component water-based acrylic waterproof coating. This coating uses pure acrylic emulsion It is made of polyacrylic acid emulsion and multi-component polyacrylic acid emulsion as the base material, mixed with a variety of additives and inorganic fillers. After coating, a tough and elastic waterproof membrane with strong adhesion can be formed, which together with the base layer forms a complete waterproofing system combining rigidity and softness to adapt to various deformations of the structure and achieve long-term waterproofing and impermeability. This product can be made into various colors as needed.
2. Product Features
Can be applied directly on wet or dry substrates of various materials.
The coating is tough and strong, water-resistant, resistant to high and low temperatures, and has good anti-aging properties. Especially in terms of UV resistance, it is better than general waterproof products.
Strong adhesion and good extensibility, optional colors.
Single component, simple construction and short construction period.
Non-toxic and odorless, it is a substitute for solvent-based waterproof coatings such as polyurethane coatings that are currently commonly used.
A variety of colors can be added to make it a decorative waterproof coating.
Three scopes of application
This product is widely used in cast-in-place concrete roofs, walls, asbestos cement tile roofs, indoor bathrooms, warehouses and other parts to renovate and repair leaks in old building surfaces for waterproofing and moisture-proofing. It can also be used as a protective layer for other waterproof layers.
Four main technical indicators implementation standards/polymer emulsion architectural waterproof coating
Technical indicators
Type I technical indicators Type II
Solid content
Tack drying time
Drying time
Tensile strength
Elongation at break
Low temperature flexibility (rod winding)
No cracks at ℃
No cracks at ℃< br/> Water impermeability
Water impermeability
Water impermeability
Five construction methods
Base layer treatment The base layer should be firm, firm and flat, with no sharp corners, no rust, oil stains and obvious water stains. The inner and outer angles should be made into arc shapes with cement mortar or sealing paste. The diameter of the inner angle should be larger than that of the outer angle, and the diameter of the outer angle should be larger than that of the outer angle. Cracks in the base layer and grooves left by pipe roots should be filled with sealing materials.
Base treatment agent In order to improve the adhesion, the base treatment agent should generally be applied. The base treatment agent can be prepared on site by diluting the waterproof coating with water. It is recommended to add the appropriate amount of water. For special base layers, special supporting base treatment agents can be used. The amount of base treatment agent is about m2.
The thick waterproof coating film should be painted in ~ times to form a film, and each coat can be applied after it is dry (generally, the painting directions are perpendicular to each other at intervals of ~ hours. If additional carcass reinforcement materials are required, The carcass material should be flat, wrinkle-free and soaked. The thickness of the coating film under the carcass should be no less than that of the upper coating film. The dosage and thickness of the carcass should be no less than ㎡~㎡. For a thick coating film, the amount of coating should be about is ㎡.
Six-pack transportation and storage
The product is placed in a clean, dry and airtight plastic barrel, and the packaging capacity is/barrel/barrel.
Transport is in accordance with non-dangerous goods requirements. When transporting, prevent Rain, exposure, squeezing, collision, inversion, keep the packaging intact.
The product should be stored in a ventilated, dry and cool place to prevent direct sunlight. The storage temperature should not be lower than ℃. The validity period is 1 year
Acrylic waterproof coating